Fast impregnation of glass, aramid and carbon fibres
High static and dynamic strength
Low surface tension, good adhesion and low curing shrinkage
Ideal for bonding wood, metal, Styropor® etc.
Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.
Epoxy resin L with Hardener S has similar mechanical properties to the laminating systems commonly used in aircraft construction.
Processing time: 15 minutes (100 g / 20 °C)
Mixing ratio: 100 : 40 parts by weight Epoxy Resin L : Hardener S 100 : 45 parts by volume Epoxy Resin L : Hardener S
Curing time (at 23 °C): 16 - 24 hours Cold hardening, hardens from 5 °C (low temperature hardener) Heat distortion temperature: Approx. 65 °C
Processing: It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.
Material characteristics (pure resin cured) Epoxy Resin L with Hardener S:
Flexural strength DIN EN ISO 178 in MPa
110
Bending E-modulus DIN EN ISO 178 in MPa
--
Tensile strength DIN EN ISO 527 in MPa
68
Compressive strength DIN EN ISO 14126 in MPa
116
CYTOX expert opinion on the Resin System Epoxy Resin L + Hardener S (see below under additional information): this system isnot cytotoxic (cell-damaging), important for applications in medical technology.
R&G
Epoxy Resin L + Hardener S (15 min.) kit/ 280 g
200 g Resin L + 80 g Hardener S
Item no. 1001051
108 in stock
(delivery time 1-2 days)
2,2'-[(1-methylethylidene)bis(4,1-phenyleneoxymethylene)] bisoxirane
Reaction mass of 2,2'-[methylenebis(4,1-phenyleneoxymethylene)]dioxirane and [2-({2-[4-(oxiran-2-ylmethoxy)benzyl]phenoxy}methyl)oxirane and [2,2'-[methylenebis(2,1-phenyleneoxymethylene)]dioxirane
Reaction products of hexane-1,6-diol with 2-(chloromethyl) oxirane (1:2)
IF IN EYES: Rinse continuously with water for several minutes. Remove contact lenses if present and easy to do. Continue rinsing.
P333 P313
If skin irritation or a rash occurs: Get medical advice / attention.
P501
Dispose of waste according to applicable legislation.
Special labelling of certain mixtures
EUH205
Contains epoxy constituents. May produce an allergic reaction.
Hazards identification - Hardener S
Hazard components for labelling
1,3-Benzoldimethanamine
Salicylic acid
2,2,4-trimethylhexane-1,6-diamine
Reaction products of the oligomerization andalkylation of 2-phenylpropene and phenol
Reaction mass of (1-phenylethyl)phenols and bis-(1-phenylethyl)phenols
Signal word:
Danger
Pictograms:
Hazard statements
H302
Harmful if swallowed.
H314
Causes severe skin burns and eye damage.
H317
May cause an allergic skin reaction.
H361d
Suspected of damaging the unborn child.
H411
Toxic to aquatic life with long lasting effects.
Precautionary statements
P303 P361 P353
IF ON SKIN (or hair): Remove/Take off immediately all contaminated clothing. Rinse skin with water or shower.
P305 P351 P338
IF IN EYES: Rinse continuously with water for several minutes. Remove contact lenses if present and easy to do. Continue rinsing.
P310
Immediately call a POISON CENTER or doctor / physician.
P362 P364
Take off contaminated clothing and wash it before reuse.
P405
Store locked up.
P501
Dispose of waste according to applicable legislation.
MSDS Epoxy Resin L (PDF)