Aramid honeycomb 29 kg/m³ (Aero), 1120 x 2440 mm, cell size: 3.2 mm
Light supporting material produced from aramid paper for fibre compound parts in sandwich construction
Excellent mechanical properties in relation to weight
High dimensional stability in heat and moisture
High-temperature resistance, service temperatures up to 180° C
Uniform product properties due to very good resin-paper bond
Self-extinguishing and low fume emission
Corrosion-resistant to water, oils, and paraffin
Material as per aircraft standards
With reference to weight, honeycombs have the greatest resistance to pressure among all support materials and extremely good resistance to chemicals, impact, vibration, and fatigue. They are also very flexible and thus also suitable for components with spherical roundings. Mould pressure is used to bond honeycombs. A vacuum bag is normally used.
Technical data:
Honeycomb type C1 - 3.2 - 29
Compressive strength (MPa)
Shear strength (MPa)
Shear modulus (MPa)
Production tolerances
Cell size (mm)
Density (kg/m³)
Dimensions (mm)
bare
stabilised
Length
Width
Length
Width
Length (mm)
Width (mm)
Thickness (mm)
Weight (%)
Cell size (%)
3,2
29
1120 x 2440
0,56
0,75
0,45
0,3
15,0
11,0
± 50
± 75
± 0,13
± 10
± 10
cormaster
Aramid Honeycomb -AERO- C1-3.2-29 (2440 x 1120 mm) T = 1.5 mm
L: 1120 mm (+/- 50 mm), W: 2440 mm (+/- 75 mm) = approx. 2.37 m², approx. 45 g/m²
Item no. 5003229-015-A-3
Only 3 left in stock, more on the way
(delivery time 1-2 days)
Technical Data Sheet Aramid honeycomb 29 kg/m³ (Aero) (PDF)