CARBON fibre sandwich sheets with Rohacell® 51 IG-F core

Lightweight carbon fibre sandwich sheets manufactured out of HT-carbon fibre prepregs in twill weave 2/2, with a transparent epoxy matrix and a sandwich core of Rohacell® 51 IG-F in press moulding.

R&G carbon fibre sandwich sheets could easily be milled, sawn or cut by waterjet.

Technical data of the CARBON fibre sandwich sheets:
Surface layers: Carbon fabric prepreg 200 g/m², twill weave 2/2
Sandwich core: Rohacell® 51 IG-F
Heat deflection temperature: 120 °C

ROHACELL® IG- F is a closed-cell, CFC-free rigid foam based on PMI (polymethacrylimide). The natural colour of ROHACELL® IG-F is white. ROHACELL® IG-F has a finer cellular structure but the same mechanical and thermal properties as ROHACELL® IG. Due to this finer cell structure, less resin is needed to wet the surface. The components become lighter.

Characteristics of ROHACELL® IG-F:

Density* (ISO 845) in kg/m	52
Compressive strength (ISO 844) in MPa	0.9
Tensile strength (ISO 527-2) in MPa	1.9
Shear strength(DIN 53294) in MPa	0,8
Tensile modulus (ISO 527-2) in MPa	70
Schubmodul (DIN 53294) in MPa	19
Flexural strength (ISO 1209) in MPa	1.6
Heat resistance (DIN 53424) in °C	180

* Die Dichtewerte gelten nur für vollformatige Platten mit einer Mindestdicke von 10 mm.

Carbon fibre sheet with Rohacell® 51 IG-F core (700 x 530 mm) T = 3.0 mm

Thickness of CFRP outer layer: 0.2 mm each, core material: Rohacell® 51 IG-F (156 g/m2), thickness tolerance: approx. 10 %, weight: approx. 520 g

Item no. 651-070-053-3 Short delivery time

Add to Shopping List

229,75 €

CARBON fibre sandwich sheets with Rohacell® 51 IG-F core

Carbon fibre sheet with Rohacell® 51 IG-F core (700 x 530 mm) T = 3.0 mm

Carbon fibre sheet with Rohacell® 51 IG-F core (800 x 280 mm) T = 3.0 mm