Elan-tech® ADH 891.892 NF Epoxy adhesive (dark grey), 400 ml (MR 2:1)

The Chemicals Ban Ordinance prohibits the sale of this product to private end consumers. Unfortunately, sales are only possible to resellers, professional users, and public research, investigation, and educational institutions. We regret this very much but ask for your understanding that we must comply with the legal prohibition.
Beginning August 24, 2023, adequate training must be provided by the employer prior to industrial or commercial use.

Elan-tech® ADH 891.892 NF from Elantas is a temperature-resistant high-performance adhesive based on epoxy resin for bonding CFRP and GFRP materials, wood, glass, ceramics, rigid foams, as well as FE and non-ferrous metals in automotive construction and sports equipment.

This high-performance adhesive is an unfilled and stable 2 component epoxy resin adhesive. The adhesive complies with RoHS (EU Directive 2002/95/EC) and RoHS Directive 2011/65/EU (RoHS 2).

Due to its thixotropic formulation thick, uneven and even vertical adhesive joints can be achieved.

• High lap shear strength (up to 39 MPa with CFK cured 2 h over 80 °C according to ASTM D 1002)
• Very high impact and peel strength
• Good thermal resistance
• Thixotropic formulation
• Low exothermic reaction and shrinkage
• Solvent-free

Processing:
Processing is very easy due to the application with a dosing gun. This also eliminates mixing errors. Elan-tech® ADH 891.892 NF cures at room temperature or elevated temperatures. Post-curing at elevated temperatures is required to achieve maximum temperature resistance.

Technical data (averages):
Processing time (25 °C): 135 minutes*
Processing time (25 °C, 40 mm, 100 ml): 15-25 minutes
Handling strength (23 °C)**: 4 hours
Viscosity: 300.000 to 550.000 MPas
Maximal gap fill: 5 mm
Colour: Dark grey
Elongation at break: 6 %
Heat resistance: 24 h / 23 °C = 60 °C; 2 h / 80 °C = 85 °C
Flexural strength: 80 MPa
Bending modulus: 2200 MPa
Tensile strength: 54 MPa
Compressive strength: 58 %

*2 mm application at 25 °C with good wetting of the surfaces to be bonded. The processing time is reduced accordingly for thicker coatings and the resulting exothermic (reaction heat).
** Curing time until a minimum tensile shear strength of 1 MPa is reached on aluminum.

Please order the dosing gun for 400 ml double cartridges (MR 2:1) (Order no 153997-1) separately.

References of the boat building industry:
Wally Europe (Italy & Tunisia), the Baglietto Group (Cantieri di Pisa, W.Magic, General Bateaux), Comar (Italy), Indiana Yachting (Italy), CMR (Italy), Cantieri Soleri (Italy), Cantieri Galetti (Italy)

References of the automobile industry:
Ferrari (Italy), Dallara (Italy), Camattini Meccanica (Italy), Škoda (Czech Republic), Fiat (Italy), Volkswagen (South Africa), TataMotors (India)

Conversion of SI units: 1 MPa (Megapascal) = 1 N/mm² = 0,102 kg/mm²